| PETG Z6002 伊斯曼化学公司 物性数据13728267595 |
| 暂无此原料描述部分┄ |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||
| 基本性能 | 比重 | --- | D792 | 1.2 | --- | ||||||||
| 相比于流动态的膜收缩，3.2-mm（0.125in./in.），厚度 | --- | D955 | 0.002-0.006mm/mm（0.002-0.006in./in.） | --- | |||||||||
| 物理性能 | 光雾 | --- | D1003 | 0.3% | --- | ||||||||
| 一般透过率 | --- | D1003 | 89% | --- | |||||||||
| 总透过率 | --- | D1003 | 91% | --- | |||||||||
| 机械性能 |
| --- |
|
| --- | ||||||||
| --- |
|
| --- | |||||||||
| 挠曲模量 | --- | D790 | 2000MPa(2.9×105 psi) | --- | |||||||||
| 挠曲屈服强度 | --- | D790 | 69MPa(10000 psi) | --- | |||||||||
| 洛氏硬度 | R刻度 | D785 | 103 | --- | |||||||||
|
|
|
| --- | |||||||||
|
|
|
| --- | |||||||||
| --- |
|
| --- | |||||||||
| --- |
|
| --- | |||||||||
| --- |
|
| --- | |||||||||
| 拉伸模量 | --- | ISO 527 | 1800MPa | --- | |||||||||
| 挠曲模量 | --- | ISO 178 | 1850MPa | --- | |||||||||
| 屈挠强度 | --- | ISO 178 | 65MPa | --- | |||||||||
|
|
|
| --- | |||||||||
| 加工性能 | 干燥温度 | --- | --- | 70℃(160�H) | --- | ||||||||
| 干燥时间 | --- | --- | 6小时 | --- | |||||||||
| 加工熔融温度 | --- | --- | 230-280℃(450-530�H) | --- | |||||||||
| 塑膜温度 | --- | --- | 15-30℃(60-80�H) | --- | |||||||||
| 热 性 能 |
| --- |
|
| --- | ||||||||