| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 比浓度对数粘度(膜)d | --- | EMN-A-AC-G-V-1 | 0.70 | --- |
| 试验膜厚度 | --- | D374 | 250微米(10mil) | --- |
| 密度 | --- | D1505 | 1.27g/cm3 | --- |
| 光雾 | --- | D1003 | 0.8% | --- |
| 光泽 | @45o | D2457 | 108 | --- |
| 透明度 | --- | D1746 | 85% | --- |
| 一般透过率 | --- | D1003 改性 | 89% | --- |
| 总透过率 | --- | D1003 改性 | 91% | --- |
| 透湿率e | --- | F372 | 6g/m2?4h(0.4g/100in.2?4h) | --- |
| --- | | rame="void">| 49 cm3 m/m2?4h tm(125 cm3 ll/100in.24h tm) | | 10 cm3 m/m2?4h tm(25 cm3 ll/100in.24h tm) | | --- |
| 物理性能 | rame="void">| 埃尔曼多夫抗撕裂性 | M.D. | | T.D. | | --- | | rame="void">| 13.7N(1400gf) | | 16.7N(1700gf) | | --- |
rame="void">| PPT抗撕裂性 | M.D. | | T.D. | | --- | | rame="void">| 93N(21 1bf) | | 93N(21 1bf) | | --- |
rame="void">| 抗撕裂传播,剖层撕裂方法 | M.D. | | M.D. | | T.D. | | T.D. | | rame="void">| @254mm/min(10in./min) | | @254mm/min(10in./min) | | @254mm/min(10in./min) | | @254mm/min(10in./min) | | rame="void">| D1938 | | D1938 | | D1938 | | D1938 | | rame="void">| 9.1N(2.1 1bf) | | 36N/mm(205 1bf/in.) | | 9.1N(2.1 1bf) | | 36N/mm(205 1bf/in.) | | --- |
rame="void">| 抗撕裂性,裤形撕裂方法 | M.D. | | T.D. | | rame="void">| 200mm/min | | 200mm/min | | rame="void">| ISO 6383-1 | | ISO 6383-1 | | rame="void">| 36N/mm(205 1bf/in.) | | 36N/mm(205 1bf/in.) | | --- |
rame="void">| 抗张强度@屈服 | M.D. | | T.D. | | --- | | rame="void">| 52MPa(7500psi) | | 52MPa(7500psi) | | --- |
rame="void">| 抗张强度@断裂 | M.D. | | T.D. | | --- | | rame="void">| 59MPa(8600psi) | | 55MPa(8000psi) | | --- |
rame="void">| 屈服伸长 | M.D. | | T.D. | | --- | | | --- |
rame="void">| 断裂伸长 | M.D. | | T.D. | | --- | | | --- |
rame="void">| 拉伸模量 | M.D. | | T.D. | | --- | | rame="void">| 1900MPa(2.8×105 psi) | | 1900MPa(2.8×105 psi) | | --- |
rame="void">| 瞬间冲击f | @23℃(73?H) | | @-18℃(0?H) | | --- | rame="void">| D1709A,改性 | | D1709A,改性 | | | --- |
| 机械性能 | 比重 | --- | ASTM D792 | 1.27 | --- |